产品参数性能项目试验条件[状态]测试方法测试数据数据单位吸水率24h，in 23℃ASTM D-5700.20%透光率厚度3mmASTM D-100388%阻燃性厚度1.47mm (厚度3.05mm )UL 9494V-2比重ASTM D-7921.20折射率ASTM D-5421.585洛氏硬度ASTM D-78577M标度拉伸率(屈服点)-ASTM D-6386-拉伸率(断裂点)-ASTM D-638140-弯曲模量ASTM D-7902230(22700)Mpa(kgf/cm2)拉伸强度(屈服点)-ASTM D-63861(620)Mpa(kgf/cm2)拉伸强度(断裂点)-ASTM D-63881(830)Mpa(kgf/cm2)拉伸模量ASTM D-6382120(21600)Mpa(kgf/cm2)弯曲强度ASTM D-79090(915)Mpa(kgf/cm2)压缩强度ASTM D-69576(770)Mpa(kgf/cm2)耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-256140(14)j/m(kgf.cm/cm)耐冲击强度值艾氏、带缺口厚度3.2mmASTM D-256880(90)j/m(kgf.cm/cm)体积电阻率ASTM D-25731016Ω.cm绝缘破坏强度快速加压值厚度1.6mmASTM D-14930KV/mm介电率60Hz(106Hz)ASTM D-1502.95(2.9)耐导电径迹性CTIIEC 112300V耐电弧性ASTM D-495110secc介电正切60Hz(106Hz)ASTM D-1500.0004(0.009)成型收缩率流动方向(垂直方向)ASTM D-9550.5～0.7%线膨胀系数流动方向(垂直方向)ASTM D-696710-5cm/cm/℃负荷挠曲温度负荷0.451MPa(4.6kgf/cm)ASTM D-648143℃温度指数(电学式)厚度1.47mmUL 746B125°C温度指数(冲击式)厚度1.47mmUL 746B115°C温度指数(非冲击式)厚度1.47mmUL 746B125°C负荷挠曲温度负荷1.813MPa(18.6kgf/cm)ASTM D-648143℃
长期原包各系列工程塑胶、通用塑胶、热塑弹性体等塑胶原料，货真价实、质量有保证、诚信经营，重信誉、守合同，互利互赢共同促进发展为目的。注：我司可提供产品物性参数表，UL黄卡、SGS、ROHS报告等出厂证明，联系人：何先生； 手机：15017036185 ，欢迎您的来电咨询！！！
PC塑胶原料通称聚碳酸酯.聚碳酸酯英文名称为Polycabonate，简称PC，它是一类分子链中含有碳酸酯结构的高分子化合物及以它为基础而制得的各种材料的总称。按分子结构中所带酯基不同可以分为脂肪族、脂环族、芳香族和脂肪－芳香族等几大类。并以双酚A型聚碳酸脂为最重要，分子量通常为3－10万。在无特别说明情况下，通常所说的聚碳酸脂都指双酚A型聚碳酸酯及其改性品种。由于其优良的机械性能，俗称防弹胶。
为非结晶性热塑性塑料
1、具高强度及弹性系数、高冲击强度、使用温度范围广。
2、高度透明性及自由染色性。
3、H.D.T.高。
4、电气特性优。
5、无味无臭对人体无害符合卫生安全。
6、成形收缩率低、尺寸安定性良好 。
电子电器：CD片、开关、家电外壳、信号筒、电话机。
汽 车： 保险杆、分电盘、安全玻璃。
工业零件：照相机本体、机具外壳、安全帽、潜水镜、安全镜片。
耐热，抗冲击，阻燃，在普通使用温度内都有良好的机械性能。同性能接近聚甲基相比，聚碳酸酯的耐冲击性能好，折射率高，加工性 能好，不需要添加剂就具有UL94 V-0级阻燃性能。但是聚甲基相对聚碳酸酯价格较低，并可通过本体聚合的方法生产大型的器件。随着聚碳酸酯生产规模的日益扩大，聚碳酸酯同聚甲 基之间的价格差异在日益缩小。聚碳酸酯的耐磨性差。一些用于易磨损用途的聚碳酸酯器件需要对表面进行特殊处理。